| Fampitahana vy volondavenona | Microstructure（Ampahany volume）（％） | |||
| Sina（GB/T 9439) | ISO 185 | ASTM A48/A48M | EN 1561 | Matrix Structure |
| HT100 (HT10-26) | 100 | No.20 F11401 | EN-GJL-100 | perlite: 30-70%, tapa-kazo matevina; Ferrite: 30-70%; Binary Phosphorus Eutectic: ＜7％ |
| HT150 (HT15-33) | 150 | No.25A F11701 | EN-GJL-150 | Pearlite: 40-90%, tapa-kazo matevina; Ferrite: 10-60%; Binary Phosphorus Eutectic: <7％ |
| HT200 (HT20-40) | 200 | No.30A F12101 | EN-GJL-200 | Pearlite: ＞95％, tapa-kazo antonony; Ferrite＜5％; Binary Phosphorus Eutectic＜4％ |
| HT250 (HT25-47) | 250 | No.35A F12401 No.40A F12801 | EN-GJL-250 | perlite: ＞98％ tapa-kazo manify; Binary Phosphorus Eutectic: <2％ |
| HT300 (HT30-54) | 300 | No.45A F13301 | EN-GJL-300 | perlite: ＞98％ tapa-kazo manify; Binary Phosphorus Eutectic: <2％ |
| HT350 (HT35-61) | 350 | No.50A F13501 | EN-GJL-350 | perlite: ＞98％ tapa-kazo manify; Binary Phosphorus Eutectic: <1％ |
Ny toetra magnetika amin'ny vy vita amin'ny volondavenona dia miovaova be, manomboka amin'ny permeability ambany sy ny hery fanerena ambony mankany amin'ny permeability ambony sy ny hery fanerena ambany. Ireo fiovana ireo dia miankina indrindra amin'ny firafitry ny vy vita amin'ny volondavenona. Manampy singa alloying mba hahazoana ny ilaina andriamby fananana dia tratra amin'ny alalan'ny fanovana ny firafitry ny volondavenona vy.
Ferrite dia manana permeability andriamby ambony sy ambany hysteresis very; Ny perlite dia mifanohitra amin'izany, manana permeability magnetika ambany izy ary fahaverezan'ny hysteresis lehibe. Ny perlite dia miforona ho ferrite amin'ny alàlan'ny fitsaboana hafanana, izay mety hampitombo in-efatra ny permeability magnetika. Ny fampitomboana ny voamaina ferrite dia mety hampihena ny fahaverezan'ny hysteresis. Ny fisian'ny simenitra dia hampihena ny hakitroky ny flux andriamby, permeability sy ny remanence, ary hampitombo ny permeability sy ny hysteresis very. Ny fisian'ny grafita maranitra dia hampihena ny remanence. Ny fiovana avy amin'ny graphite karazana A (grafita miendrika flake izay mizara mitovy tsy misy tari-dalana) mankany amin'ny graphite D-karazana (grafita mihodinkodina tsara miaraka amin'ny fizarana tsy misy tari-dalana eo anelanelan'ny dendrites) dia mety hampitombo be ny induction magnetika sy ny hery fanerena. .
Alohan'ny hahatongavana amin'ny mari-pana manakiana tsy misy magnetika, ny fiakaran'ny mari-pana dia mampitombo be ny fahafahan'ny andriamby amin'ny vy vita amin'ny volondavenona. Ny teboka Curie amin'ny vy madio dia ny mari-pana fifindran'ny α-γ amin'ny 770 ° C. Raha 5% ny isan-jaton'ny silisiôna, dia hahatratra 730°C ny teboka Curie. Ny mari-pana Curie point amin'ny simenitra tsy misy silisiôma dia 205-220 ° C.
Ny firafitry ny matrix amin'ny vy vita amin'ny vy vita amin'ny volondavenona matetika dia perlite, ary ny permeability ambony indrindra dia eo anelanelan'ny 309-400 μH / m.
Toetran'ny andriamby amin'ny vy vita amin'ny volondavenona | |||||||
| Code of Grey Iron | Famoronana simika (%) | ||||||
| C | Si | Mn | S | P | Ni | Cr | |
| A | 3.12 | 2.22 | 0.67 | 0.067 | 0.13 | <0.03 | 0.04 |
| B | 3.30 | 2.04 | 0.52 | 0.065 | 1.03 | 0.34 | 0.25 |
| C | 3.34 | 0.83 - 0.91 | 0.20 - 0.33 | 0,021 - 0,038 | 0,025 - 0,048 | 0.04 | <0.02 |
| Properties andriamby | A | B | C | ||||
| perlite | Ferrite | perlite | Ferrite | perlite | Ferrite | ||
| Carbide Carbon w(%) | 0.70 | 0.06 | 0.77 | 0.11 | 0.88 | / | |
| Remanence / T | 0.413 | 0.435 | 0.492 | 0.439 | 0.5215 | 0.6185 | |
| Hery fanerena / A•m-1 | 557 | 199 | 716 | 279 | 637 | 199 | |
| Very Hysteresis / J•m-3•Hz-1 (B=1T) | 2696 | -696 | 2729 | 1193 | 2645 | 938 | |
| Herin'ny sahan'andriamby / kA•m-1 (B=1T) | 15.9 | -5.9 | 8.7 | 8.0 | 6.2 | 4.4 | |
| Max. Fahavitrihana andriamby / μH•m-1 | 396 | 1960 | 353 | 955 | 400 | 1703 | |
| Ny herin'ny sahan'andriamby rehefa Max. Fihetsiketsehana andriamby / A•m-1 | 637 | 199 | 1035 | 318 | 1114 | 239 | |
| Resistivity / μΩ•m | 0.73 | 0.71 | 0.77 | 0.75 | 0.42 | 0.37 | |
Ireto manaraka ireto ny toetra mekanika amin'ny vy vita amin'ny grey:
Toetra mekanika amin'ny vy vita amin'ny volondavenona | |||||||
| Ireo singa mifandraika amin'ny DIN EN 1561 | ohatra | Unit | EN-GJL-150 | EN-GJL-200 | EN-GJL-250 | EN-GJL-300 | EN-GJL-350 |
| EN-JL 1020 | EN-JL 1030 | EN-JL 1040 | EN-JL 1050 | EN-JL 1060 | |||
| Faharetana amin'ny sintona | Rm | MPA | 150-250 | 200-300 | 250-350 | 300-400 | 350-450 |
| 0,1% ny tanjaky ny vokatra | Rp0,1 | MPA | 98-165 | 130-195 | 165-228 | 195-260 | 228-285 |
| Elongation Hery | A | % | 0,3 – 0,8 | 0,3 – 0,8 | 0,3 – 0,8 | 0,3 – 0,8 | 0,3 – 0,8 |
| Hery fanerena | σdB | MPa | 600 | 720 | 840 | 960 | 1080 |
| 0,1% Hery fanerena | σd0,1 | MPa | 195 | 260 | 325 | 390 | 455 |
| Hery flexural | σbB | MPa | 250 | 290 | 340 | 390 | 490 |
| Schuifspanning | σaB | MPa | 170 | 230 | 290 | 345 | 400 |
| Hetezana adin-tsaina | TtB | MPa | 170 | 230 | 290 | 345 | 400 |
| Modules ny elasticité | E | GPa | 78 – 103 | 88 – 113 | 103 – 118 | 108 – 137 | 123 – 143 |
| laharana Poisson | v | – | 0,26 | 0,26 | 0,26 | 0,26 | 0,26 |
| Brinell hamafin'ny | HB | 160 – 190 | 180 – 220 | 190 – 230 | 200 – 240 | 210 – 250 | |
| ductility | σbW | MPa | 70 | 90 | 120 | 140 | 145 |
| Ny fihenjanana sy ny fiovan'ny tsindry | σzdW | MPa | 40 | 50 | 60 | 75 | 85 |
| Hery manapaka | Klc | N/mm3/2 | 320 | 400 | 480 | 560 | 650 |
| hakitroky | g/cm3 | 7,10 | 7,15 | 7,20 | 7,25 | 7,30 | |